Type Lee, W.-B.; Hong, S.-G.; Park, C.-G.; Park, S.-H.
  Publication Carbide precipitation and high-temperature strength of hot-rolled high-strength, low-alloy steels containing Nb and Mo Volume Journal Article
Pages 2002
  Abstract Metallurgical and Materials Transactions A  
  Corporate Author  
Publisher 33  
Editor 6
  Summary Language 1689-1698 Series Editor  
Abbreviated Series Title Abstract  The effects of a Mo addition on both the precipitation kinetics and high-temperature strength of a Nb carbide have been investigated in the hot-rolled high-strength, low-alloy (HSLA) steels containing both Nb and Mo. These steels were fabricated by four-pass hot rolling and coiling at 650C, 600C, and 550C. Microstructural analysis of the carbides has been performed using field-emission gun transmission electron microscopy (TEM) employing energy-dispersive X-ray spectroscopy (EDS). The steels containing both Nb and Mo exhibited a higher strength at high temperatures (â¼600 C) in comparison to the steel containing only Nb. The addition of Mo increased the hardenability and led to the refinement of the bainitic microstructure. The proportion of the bainitic phase increased with the increase of Mo content. The TEM observations revealed that the steels containing both Nb and Mo exhibited fine (<10 nm) and uniformly distributed metal carbide (MC)-type carbides, while the carbides were coarse and sparsely distributed in the steels containing Nb only. The EDS analysis also indicated that the fine MC carbides contain both Nb and Mo, and the ratio of Mo/Nb was higher in the finer carbides. In addition, electron diffraction analysis revealed that most of the MC carbides had one variant of the B-N relationship ((100)MC//(100)ferrite, [011]MC//[010]ferrite) with the matrix, suggesting that they were formed in the ferrite region. That is, the addition of Mo increased the nucleation sites of MC carbides in addition to the bainitic transformation, which resulted in finer and denser MC carbides. It is, thus, believed that the enhanced high-temperature strength of the steels containing both Nb and Mo was attributed to both bainitic transformation hardening and the precipitation hardening caused by uniform distribution of fine MC particles.
  Series Issue ISSN  
Medium
  Expedition Notes  
Call Number  
Contribution Id  
Serial URL ISBN  
no NU @ p-kolli @ 9838
Permanent link to this record
Select All    Deselect All
 |   | 
Details
   print

Personal tools
Seidman Group
Atom-Probe Tomography
Search
Quick Search: